Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 40
Page 86
... cells ; even thin biofilms of bacteria ( 107 cells / cm2 ) can show higher resistance than the same , unattached , cells / 6 / . This could suggest that it is the altered physiological state of sessile cells which renders them less ...
... cells ; even thin biofilms of bacteria ( 107 cells / cm2 ) can show higher resistance than the same , unattached , cells / 6 / . This could suggest that it is the altered physiological state of sessile cells which renders them less ...
Page 87
... cells embedded within the biofilm . 2. IMPROVING BIOCIDE ACTIVITY AGAINST SESSILE ORGANISMS Whatever the mechanism , there is no doubt that , in practical terms , the majority of biocides do not effectively penetrate biofilms ...
... cells embedded within the biofilm . 2. IMPROVING BIOCIDE ACTIVITY AGAINST SESSILE ORGANISMS Whatever the mechanism , there is no doubt that , in practical terms , the majority of biocides do not effectively penetrate biofilms ...
Page 117
... cells both when CP was immediately after the immersion and 3 h later . The effect of temperature on metabolic ... cells were found in shorter exposure times . An important diminution of the attached cells with respect to the controls was ...
... cells both when CP was immediately after the immersion and 3 h later . The effect of temperature on metabolic ... cells were found in shorter exposure times . An important diminution of the attached cells with respect to the controls was ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate