Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 55
Page 34
... biofilm on the corrosion potential would make the initiation of crevice corrosion beneath the biofilm more likely . In a recent paper Dexter and Lin / 4 / considered the influence of the biofilm on cathodic protection in two parts : i ...
... biofilm on the corrosion potential would make the initiation of crevice corrosion beneath the biofilm more likely . In a recent paper Dexter and Lin / 4 / considered the influence of the biofilm on cathodic protection in two parts : i ...
Page 86
... biofilm - penetrating ability and biocide tests must include the determination of this parameter . In addition , laboratory tests for biocide efficacy must take into account the operational characteristics of the system . A careful ...
... biofilm - penetrating ability and biocide tests must include the determination of this parameter . In addition , laboratory tests for biocide efficacy must take into account the operational characteristics of the system . A careful ...
Page 88
3. SPECIFIC BIOCIDES AGAINST BACTERIAL BIOFILMS Of the biocides currently in the market , the isothiazolones appear to be excellent biofilm penetrants , but they have the disadvantages of being inhibited by hydrogen sulphide and being ...
3. SPECIFIC BIOCIDES AGAINST BACTERIAL BIOFILMS Of the biocides currently in the market , the isothiazolones appear to be excellent biofilm penetrants , but they have the disadvantages of being inhibited by hydrogen sulphide and being ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate