Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 50
Page 258
... ASTM tests were established to determine the quality of the mill supplied material and were never meant for ranking ... ASTM G - 28A Boiling 24 36 168 ASTM G - 28B Boiling 4 7 55 Green Death Boiling 5 26 G - 28A- G - 28B- Green Death 50 ...
... ASTM tests were established to determine the quality of the mill supplied material and were never meant for ranking ... ASTM G - 28A Boiling 24 36 168 ASTM G - 28B Boiling 4 7 55 Green Death Boiling 5 26 G - 28A- G - 28B- Green Death 50 ...
Page 268
... ASTM G - 28A ASTM G -- 28B . Selective Explosive Bond Area of Alloy C - 276 168 , 173 44.42 Unbonded Area 182 53 • Typical Range of Values For Alloy C - 276 160-360 40-80 Furthermore the chemical composition of alloy C - 276 is uniform ...
... ASTM G - 28A ASTM G -- 28B . Selective Explosive Bond Area of Alloy C - 276 168 , 173 44.42 Unbonded Area 182 53 • Typical Range of Values For Alloy C - 276 160-360 40-80 Furthermore the chemical composition of alloy C - 276 is uniform ...
Page 280
... ASTM specifications : ASTM G - 28 METHOD A : Uniform corrosion rates are shown in Figure 1. Alloy 59 with 0.6 mm / year ( 24 mpy ) is clearly superior to Alloy 22 with 0.9 mm / year ( 36 mpy ) . Alloy C - 4 and Alloy C - 276 due to ...
... ASTM specifications : ASTM G - 28 METHOD A : Uniform corrosion rates are shown in Figure 1. Alloy 59 with 0.6 mm / year ( 24 mpy ) is clearly superior to Alloy 22 with 0.9 mm / year ( 36 mpy ) . Alloy C - 4 and Alloy C - 276 due to ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate