Building Science Series, Issues 0-20 |
From inside the book
Results 1-5 of 69
Page
... Cured Mortars . 55 cents BSS9 . Thermal - Shock Resistance for Built - Up Membranes . 20 cents BSS10 . Field Burnout Tests of Apartment Dwelling Units . 25 cents BSS11 . Fire Resistance of Steel Deck Floor Assemblies . 25 cents BSS12 ...
... Cured Mortars . 55 cents BSS9 . Thermal - Shock Resistance for Built - Up Membranes . 20 cents BSS10 . Field Burnout Tests of Apartment Dwelling Units . 25 cents BSS11 . Fire Resistance of Steel Deck Floor Assemblies . 25 cents BSS12 ...
Page 2
... cured in a moist cabinet at 95-100 percent relative humidity for 24 hours , after which the molds were stripped and the length of the prisms measured . The speci- mens were stored in water and length measure- ments were made at 7 , 14 ...
... cured in a moist cabinet at 95-100 percent relative humidity for 24 hours , after which the molds were stripped and the length of the prisms measured . The speci- mens were stored in water and length measure- ments were made at 7 , 14 ...
Page 38
... cured 2 - inch mortar cubes at the respec- tive ages . The " F " values are the ratios of the reduction in variance due to the fitted constants associated with the independent variables to the variance obtained from the residuals after ...
... cured 2 - inch mortar cubes at the respec- tive ages . The " F " values are the ratios of the reduction in variance due to the fitted constants associated with the independent variables to the variance obtained from the residuals after ...
Page 10
... cured cement . From the data presented here , it is obvious that the substitution of Fe2O3 for Al2O3 in the calcium aluminate hydrates causes relatively slight changes in their measurable characteristics , especially over the range ...
... cured cement . From the data presented here , it is obvious that the substitution of Fe2O3 for Al2O3 in the calcium aluminate hydrates causes relatively slight changes in their measurable characteristics , especially over the range ...
Page
... Cured Mortars R. L. Blaine , H. T. Arni , and M. R. DeFore Building Research Division Institute for Applied Technology National Bureau of Standards Washington , D.C. 20234 DEPARTMENT NATIONAL OF COMMERCE BUREAU OF STANDARDS Building ...
... Cured Mortars R. L. Blaine , H. T. Arni , and M. R. DeFore Building Research Division Institute for Applied Technology National Bureau of Standards Washington , D.C. 20234 DEPARTMENT NATIONAL OF COMMERCE BUREAU OF STANDARDS Building ...
Other editions - View all
Common terms and phrases
28 days acid AE+NAE cements air content annular specimens apparatus associated ASTM autoclave building materials Building Science Series Bureau of Standards Calculated contribution Calculated range Cement and Concrete cements with respect cents coef Coef./s.d. ratio less coefficients computed Concrete Properties cured effect enamels equations relating expansion values exposure felt FIGURE fire floor Frequency distribution gypsum heat of hydration ignition increase indicated insulating Interrelations Between Cement K₂O Kure Beach laboratory load loss on ignition measurements membrane mixing Modacrylic moisture mold mortar Na2O NAE cements National Bureau NBS Building obtained optical density OREX orifice oxide percent Polyamide portland cement presented in table pressure procedure relationship roofing S.D. values sample saturant significant silica smoke steel structural sulfate surface temperature test methods thermal thermocouples tion trace elements turbidimeter types various independent variables WAGN WAGR water-cement ratio weight
Popular passages
Page 8 - In no case does such identification imply recommendation or endorsement by the National Bureau of Standards , nor does it imply that the...
Page 7 - Handbooks — Recommended codes of engineering and industrial practice (including safety codes) developed in cooperation with interested industries, professional organizations, and regulatory bodies. Special Publications...
Page 2 - ... advisory services to government agencies on scientific and technical problems; invention and development of devices to serve special needs of the Government; and the development of standard practices, codes, and specifications.