Corrosion Reviews, Volumes 11-13Scientific Publications Division, Freund Publishing House, 1993 |
From inside the book
Results 1-3 of 77
Page 46
... specimens from one material grade . Material grades were S31726 , N08904 , N08926 , N08028 , N06985 , N06625 - Gr.1 ... specimens 100 x 50mm , as supplied ( mill finish ) 2 2 specimens 100 x 50mm , MMA welded 3 1 specimen 100 x ...
... specimens from one material grade . Material grades were S31726 , N08904 , N08926 , N08028 , N06985 , N06625 - Gr.1 ... specimens 100 x 50mm , as supplied ( mill finish ) 2 2 specimens 100 x 50mm , MMA welded 3 1 specimen 100 x ...
Page 52
... specimens with and without weld showed any indication of stress corrosion cracking . A summarized evaluation is given in Table 8 . Results of sheet specimens 70 ° C , 0.1 m / s . These specimens were covered with calcareous deposits ...
... specimens with and without weld showed any indication of stress corrosion cracking . A summarized evaluation is given in Table 8 . Results of sheet specimens 70 ° C , 0.1 m / s . These specimens were covered with calcareous deposits ...
Page 11
... specimens . Each digitized ultrasonic signal was averaged over 64 readings to improve the signal - to - noise ratio . One specimen was then destructively tested while the rest of the specimens were put back into the water until the ...
... specimens . Each digitized ultrasonic signal was averaged over 64 readings to improve the signal - to - noise ratio . One specimen was then destructively tested while the rest of the specimens were put back into the water until the ...
Contents
Scale Formation During Nucleate Boiling A Review | 26 |
Change in Boiling Mechanism with Time | 33 |
Heat Transfer Models in the Presence of Deposit | 43 |
38 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion AISI alkali Alloy 59 aluminium anodic anticorrosive application ASTM austenitic bacteria behaviour biocide biofilm biofouling boiling bubble carbon steel cathodic protection chemical chloride chromate composition concentration concrete cooling water corrosion inhibitors corrosion rate corrosion resistance cost crevice corrosion current density decrease deposit effect electrochemical electrode Engineering environment erosion evaluation experimental exposure fluid formation fouling growth heat exchangers heat flux heat transfer coefficient heat transfer surface impact inclusions increase industrial ions iron laboratory layer marine materials mechanism metal surface method Michael Schorr NACE nickel nucleation obtained oxide oxygen ozone paint particles passive film phosphate coatings pigment pitting corrosion pitting potential polarization present Pseudomonas fluorescens rebars reduced scale sea water seawater shear slurry solubility solution specimens stainless steel stress corrosion cracking structure Table Technology temperature thermal thickness values velocity W/mē weld zinc phosphate