Corrosion Reviews, Volumes 11-13Scientific Publications Division, Freund Publishing House, 1993 |
From inside the book
Results 1-3 of 30
Page 146
... rust " , were observed on the surface of the pure zinc coatings after about twelve months exposure . The zinc - nickel alloy coatings remained dull grey in appearance but some white corrosion products formed on the experimental zinc ...
... rust " , were observed on the surface of the pure zinc coatings after about twelve months exposure . The zinc - nickel alloy coatings remained dull grey in appearance but some white corrosion products formed on the experimental zinc ...
Page 148
... rust of a 15μm thick coating is ex . nded from 220 days to 1060 days if 5 % magnesium is incorporated in the coating . The time to first rust for zinc - nickel coatings prepared by brush plating was found to be less than ...
... rust of a 15μm thick coating is ex . nded from 220 days to 1060 days if 5 % magnesium is incorporated in the coating . The time to first rust for zinc - nickel coatings prepared by brush plating was found to be less than ...
Page 149
Time to first rust . days 1000 500 A Laboratory bath Brush plated Proprietary bath 10 Nickel Content w / o 20 30 Fig . 2 : Effect of nickel content on the time to first rust for laboratory prepared and proprietary electrodeposited zinc ...
Time to first rust . days 1000 500 A Laboratory bath Brush plated Proprietary bath 10 Nickel Content w / o 20 30 Fig . 2 : Effect of nickel content on the time to first rust for laboratory prepared and proprietary electrodeposited zinc ...
Contents
Scale Formation During Nucleate Boiling A Review | 26 |
Change in Boiling Mechanism with Time | 33 |
Heat Transfer Models in the Presence of Deposit | 43 |
34 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion AISI alkali Alloy 59 aluminium anodic anticorrosive application ASTM austenitic bacteria behaviour biocide biofilm biofouling boiling bubble carbon steel cathodic protection cells chemical chloride chromate composition concentration concrete cooling water corrosion inhibitors corrosion rate corrosion resistance cost crevice corrosion current density decrease deposit effect electrochemical electrode Engineering environment erosion evaluation experimental exposure fluid formation fouling growth heat exchangers heat flux heat transfer coefficient heat transfer surface impact inclusions increase industrial ions iron laboratory layer marine materials mechanism metal surface method Michael Schorr NACE nickel nucleation obtained oxide oxygen ozone paint particles passive film phosphate coatings pigment pitting corrosion polarization present Pseudomonas fluorescens rebars reduced samples scale sea water seawater shear slurry solubility solution specimens stainless steel stress corrosion cracking structure Table Technology temperature thermal thickness tube values velocity W/m² weld zinc phosphate