Corrosion Reviews, Volumes 11-13Scientific Publications Division, Freund Publishing House, 1993 |
From inside the book
Results 1-3 of 35
Page 215
TABLE 3 CHARACTERISTICS OF PHOSPHATE COATINGS Type of coating Characteristic Iron Phosphate Zinc Phosphate Coating weight 0.16-0.80 g / m2 1.4 - 4.0 g / m2 Types Cleaner / coater Standard Organic phosphate Standard Nickel - modified Low ...
TABLE 3 CHARACTERISTICS OF PHOSPHATE COATINGS Type of coating Characteristic Iron Phosphate Zinc Phosphate Coating weight 0.16-0.80 g / m2 1.4 - 4.0 g / m2 Types Cleaner / coater Standard Organic phosphate Standard Nickel - modified Low ...
Page 217
... phosphate coatings . Machu / 25 / listed 30 such phosphate compounds identified in a phosphate coating . Neuhaus and Gebhardt / 84 / have tabulated the main phases in phosphate coatings formed on metals from baths of various phosphates ...
... phosphate coatings . Machu / 25 / listed 30 such phosphate compounds identified in a phosphate coating . Neuhaus and Gebhardt / 84 / have tabulated the main phases in phosphate coatings formed on metals from baths of various phosphates ...
Page 221
... phosphate coatings due to the presence of tightly bound carbonaceous residues formed on steel during steel making ... coatings / 100 / . Machu's / 25 / method of determination of porosity of coating by electrochemical means is based on ...
... phosphate coatings due to the presence of tightly bound carbonaceous residues formed on steel during steel making ... coatings / 100 / . Machu's / 25 / method of determination of porosity of coating by electrochemical means is based on ...
Contents
Scale Formation During Nucleate Boiling A Review | 26 |
Change in Boiling Mechanism with Time | 33 |
Heat Transfer Models in the Presence of Deposit | 43 |
34 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion AISI alkali Alloy 59 aluminium anodic anticorrosive application ASTM austenitic bacteria behaviour biocide biofilm biofouling boiling bubble carbon steel cathodic protection cells chemical chloride chromate composition concentration concrete cooling water corrosion inhibitors corrosion rate corrosion resistance cost crevice corrosion current density decrease deposit effect electrochemical electrode Engineering environment erosion evaluation experimental exposure fluid formation fouling growth heat exchangers heat flux heat transfer coefficient heat transfer surface impact inclusions increase industrial ions iron laboratory layer marine materials mechanism metal surface method Michael Schorr NACE nickel nucleation obtained oxide oxygen ozone paint particles passive film phosphate coatings pigment pitting corrosion polarization present Pseudomonas fluorescens rebars reduced samples scale sea water seawater shear slurry solubility solution specimens stainless steel stress corrosion cracking structure Table Technology temperature thermal thickness tube values velocity W/mē weld zinc phosphate