... molybdate which protects metal surfaces / 22 / . In 1962 , 1 ppm of molybdate was used to improve synergetically the protection of chromate - zinc treatments ( of lime ) . When environmental restrictions limited the use of chromates ...
... molybdate which protects metal surfaces / 22 / . In 1962 , 1 ppm of molybdate was used to improve synergetically the protection of chromate - zinc treatments ( of lime ) . When environmental restrictions limited the use of chromates ...
Page 162
... Molybdate to Deaerated Sodium Chloride Media Fig . 4 shows the influence of the addition of different amounts of molybdate species in a solution containing 0,1 mol / l NaCl . The sodium molybdate acts as a corrosion inhibitor in a ...
... Molybdate to Deaerated Sodium Chloride Media Fig . 4 shows the influence of the addition of different amounts of molybdate species in a solution containing 0,1 mol / l NaCl . The sodium molybdate acts as a corrosion inhibitor in a ...
Page 19
... molybdate component of these molybdate / phosphate coatings are easily soluble ; hence these coatings do not provide good corrosion protection and do not perform effectively under organic coatings / 12 / . More recently , black molybdate ...
... molybdate component of these molybdate / phosphate coatings are easily soluble ; hence these coatings do not provide good corrosion protection and do not perform effectively under organic coatings / 12 / . More recently , black molybdate ...
Contents
Scale Formation During Nucleate Boiling A Review | 26 |
Change in Boiling Mechanism with Time | 33 |
Heat Transfer Models in the Presence of Deposit | 43 |
34 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion AISI alkali Alloy 59 aluminium anodic anticorrosive application ASTM austenitic bacteria behaviour biocide biofilm biofouling boiling bubble carbon steel cathodic protection cells chemical chloride chromate composition concentration concrete cooling water corrosion inhibitors corrosion rate corrosion resistance cost crevice corrosion current density decrease deposit effect electrochemical electrode Engineering environment erosion evaluation experimental exposure fluid formation fouling growth heat exchangers heat flux heat transfer coefficient heat transfer surface impact inclusions increase industrial ions iron laboratory layer marine materials mechanism metal surface method Michael Schorr NACE nickel nucleation obtained oxide oxygen ozone paint particles passive film phosphate coatings pigment pitting corrosion polarization present Pseudomonas fluorescens rebars reduced samples scale sea water seawater shear slurry solubility solution specimens stainless steel stress corrosion cracking structure Table Technology temperature thermal thickness tube values velocity W/m² weld zinc phosphate