Page 86
Thermal conductivity and thermal expansion are especially important The thermal conductivity of SAF 2507 is slightly higher than that of austenitic stainless steels . This , together with increased possibilities of using thinner ...
Thermal conductivity and thermal expansion are especially important The thermal conductivity of SAF 2507 is slightly higher than that of austenitic stainless steels . This , together with increased possibilities of using thinner ...
Page 87
CORROSION RESISTANCE Two categories of corrosion are especially important for stainless steels in chloride - bearing environments - localized corrosion and stress corrosion cracking . Localized corrosion usually occurs in the form of ...
CORROSION RESISTANCE Two categories of corrosion are especially important for stainless steels in chloride - bearing environments - localized corrosion and stress corrosion cracking . Localized corrosion usually occurs in the form of ...
Page 116
Pigment / binder ratio exerts a great influence over important characteristics of coating films ( gloss , permeability , adhesion , abrasion resistance , etc. ) ; usually , this relationship is expressed as pigment volume concentration ...
Pigment / binder ratio exerts a great influence over important characteristics of coating films ( gloss , permeability , adhesion , abrasion resistance , etc. ) ; usually , this relationship is expressed as pigment volume concentration ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Scale Formation During Nucleate Boiling A Review | 26 |
Change in Boiling Mechanism with Time | 33 |
Heat Transfer Models in the Presence of Deposit | 43 |
39 other sections not shown
Other editions - View all
Common terms and phrases
acid addition adhesion alloy anodic application attack biocide biofilm bubble carbon cathodic caused characteristics chemical chloride coatings composition concentration concrete containing cooling corrosion rate corrosion resistance cost decrease density depends deposit determined effect electrochemical Engineering environment equipment erosion evaluation experimental experiments Figure flow fluid formation formed fouling growth heat transfer higher impact important improved increase industrial influence inhibitor ions iron laboratory layer lower marine materials measurements mechanism metal method natural nickel observed obtained occurs operating organic oxide ozone paint particles passive performance phosphate pigment pitting plant potential present properties protection reaction reduced References removal samples scale seawater shown shows solution specimens stainless steel strength structure studied surface Table Technology temperature thickness treatment values various weld zinc