Corrosion Reviews, Volumes 11-13Scientific Publications Division, Freund Publishing House, 1993 |
From inside the book
Results 1-3 of 25
Page 323
... erosion - corrosion " is the deterioration of material due to the simultaneous action of mechanical and electrochemical forces . Both erosion and corrosion processes probably assist each other to bring about the amount of damage which ...
... erosion - corrosion " is the deterioration of material due to the simultaneous action of mechanical and electrochemical forces . Both erosion and corrosion processes probably assist each other to bring about the amount of damage which ...
Page 326
hydrochloric acid solution slurry was higher than the pure erosion rate of the specimen in a silica sand - deionized water slurry , W. This acceleration of the erosion rate by corrosion , or a positive AW was attributed to the ...
hydrochloric acid solution slurry was higher than the pure erosion rate of the specimen in a silica sand - deionized water slurry , W. This acceleration of the erosion rate by corrosion , or a positive AW was attributed to the ...
Page 343
hydrochloric acid solution slurry was higher than the pure erosion rate of the specimen in a silica sand - deionized water slurry , W. This acceleration of the erosion rate by corrosion , or a positive AW was attributed to the ...
hydrochloric acid solution slurry was higher than the pure erosion rate of the specimen in a silica sand - deionized water slurry , W. This acceleration of the erosion rate by corrosion , or a positive AW was attributed to the ...
Contents
Scale Formation During Nucleate Boiling A Review | 26 |
Change in Boiling Mechanism with Time | 33 |
Heat Transfer Models in the Presence of Deposit | 43 |
34 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion AISI alkali Alloy 59 aluminium anodic anticorrosive application ASTM austenitic bacteria behaviour biocide biofilm biofouling boiling bubble carbon steel cathodic protection cells chemical chloride chromate composition concentration concrete cooling water corrosion inhibitors corrosion rate corrosion resistance cost crevice corrosion current density decrease deposit effect electrochemical electrode Engineering environment erosion evaluation experimental exposure fluid formation fouling growth heat exchangers heat flux heat transfer coefficient heat transfer surface impact inclusions increase industrial ions iron laboratory layer marine materials mechanism metal surface method Michael Schorr NACE nickel nucleation obtained oxide oxygen ozone paint particles passive film phosphate coatings pigment pitting corrosion polarization present Pseudomonas fluorescens rebars reduced samples scale sea water seawater shear slurry solubility solution specimens stainless steel stress corrosion cracking structure Table Technology temperature thermal thickness tube values velocity W/mē weld zinc phosphate