Corrosion Reviews, Volumes 11-13Scientific Publications Division, Freund Publishing House, 1993 |
From inside the book
Results 1-3 of 65
Page 146
... coatings after about twelve months exposure . The zinc - nickel alloy coatings remained dull grey in appearance but some white corrosion products formed on the experimental zinc alloys which contained less than 9 % nickel by weight ...
... coatings after about twelve months exposure . The zinc - nickel alloy coatings remained dull grey in appearance but some white corrosion products formed on the experimental zinc alloys which contained less than 9 % nickel by weight ...
Page 148
... coatings Coating 8μm thick 15 μm thick Time in days Time in days Electrodeposited cadmium 600 1160 Electrodeposited zinc 690 1200 IVD Aluminium peened 80 peened and passivated 990 180 140 280 Experimental IVD coatings Aluminium 120 220 ...
... coatings Coating 8μm thick 15 μm thick Time in days Time in days Electrodeposited cadmium 600 1160 Electrodeposited zinc 690 1200 IVD Aluminium peened 80 peened and passivated 990 180 140 280 Experimental IVD coatings Aluminium 120 220 ...
Page 163
... coatings . Sacrificial metal coatings are covered in Chapter 2 , noble metal coatings are in Chapters 3 and 4 , inorganic coatings in Chapter 5 , and organic coatings in Chapter 6. Each coating is described based on its classification ...
... coatings . Sacrificial metal coatings are covered in Chapter 2 , noble metal coatings are in Chapters 3 and 4 , inorganic coatings in Chapter 5 , and organic coatings in Chapter 6. Each coating is described based on its classification ...
Contents
Scale Formation During Nucleate Boiling A Review | 26 |
Change in Boiling Mechanism with Time | 33 |
Heat Transfer Models in the Presence of Deposit | 43 |
34 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion AISI alkali Alloy 59 aluminium anodic anticorrosive application ASTM austenitic bacteria behaviour biocide biofilm biofouling boiling bubble carbon steel cathodic protection cells chemical chloride chromate composition concentration concrete cooling water corrosion inhibitors corrosion rate corrosion resistance cost crevice corrosion current density decrease deposit effect electrochemical electrode Engineering environment erosion evaluation experimental exposure fluid formation fouling growth heat exchangers heat flux heat transfer coefficient heat transfer surface impact inclusions increase industrial ions iron laboratory layer marine materials mechanism metal surface method Michael Schorr NACE nickel nucleation obtained oxide oxygen ozone paint particles passive film phosphate coatings pigment pitting corrosion polarization present Pseudomonas fluorescens rebars reduced samples scale sea water seawater shear slurry solubility solution specimens stainless steel stress corrosion cracking structure Table Technology temperature thermal thickness tube values velocity W/m² weld zinc phosphate