Corrosion Reviews, Volumes 11-13Scientific Publications Division, Freund Publishing House, 1993 |
From inside the book
Results 1-3 of 82
Page 9
... behaviour of stainless steel immersed in sea water or exposed to tidal action , since it was known that stainless steels - even AISI Type 316 - were susceptible to corrosion in chloride media . The results of the research showed that ...
... behaviour of stainless steel immersed in sea water or exposed to tidal action , since it was known that stainless steels - even AISI Type 316 - were susceptible to corrosion in chloride media . The results of the research showed that ...
Page 10
... behaviour of high tensile roping steel in sea water defines a much higher limit compared with the experimental S - N curve . The analysis also reveals that techniques such as cathodic protection greatly improve fretting fatigue ...
... behaviour of high tensile roping steel in sea water defines a much higher limit compared with the experimental S - N curve . The analysis also reveals that techniques such as cathodic protection greatly improve fretting fatigue ...
Page 54
... behaviour was observed in a 1000 hours salt spray test . ZP alone led to fair and poor results in both conditions , respectively . However , a formulation based on yellow ( 10 % ) and red ( 9.2 % ) iron oxides and talc ( 8 % ) and ZP ...
... behaviour was observed in a 1000 hours salt spray test . ZP alone led to fair and poor results in both conditions , respectively . However , a formulation based on yellow ( 10 % ) and red ( 9.2 % ) iron oxides and talc ( 8 % ) and ZP ...
Contents
Scale Formation During Nucleate Boiling A Review | 26 |
Change in Boiling Mechanism with Time | 33 |
Heat Transfer Models in the Presence of Deposit | 43 |
34 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion AISI alkali Alloy 59 aluminium anodic anticorrosive application ASTM austenitic bacteria behaviour biocide biofilm biofouling boiling bubble carbon steel cathodic protection cells chemical chloride chromate composition concentration concrete cooling water corrosion inhibitors corrosion rate corrosion resistance cost crevice corrosion current density decrease deposit effect electrochemical electrode Engineering environment erosion evaluation experimental exposure fluid formation fouling growth heat exchangers heat flux heat transfer coefficient heat transfer surface impact inclusions increase industrial ions iron laboratory layer marine materials mechanism metal surface method Michael Schorr NACE nickel nucleation obtained oxide oxygen ozone paint particles passive film phosphate coatings pigment pitting corrosion polarization present Pseudomonas fluorescens rebars reduced samples scale sea water seawater shear slurry solubility solution specimens stainless steel stress corrosion cracking structure Table Technology temperature thermal thickness tube values velocity W/mē weld zinc phosphate