Corrosion Reviews, Volumes 11-13Scientific Publications Division, Freund Publishing House, 1993 |
From inside the book
Results 1-3 of 33
Page 259
for ranking alloys within the Ni - Cr - Mo family of alloys should be avoided . To further study the localized ... alloy 22 in comparison to higher molybdenum containing alloy 59 and C - 276 . In FGD systems , crevice corrosion is ...
for ranking alloys within the Ni - Cr - Mo family of alloys should be avoided . To further study the localized ... alloy 22 in comparison to higher molybdenum containing alloy 59 and C - 276 . In FGD systems , crevice corrosion is ...
Page 279
... Alloy UTS ( KSI ) 0.2 % Y.S. ( KSI ) % El Alloy C 120 58 48 Alloy C - 276 110 53 62 Alloy C - 4 116 59 55 Alloy 22 106 52 65 Alloy 59 112 55 65 Within the statistical variation the room temperature mechanical properties of Alloy C - 276 , ...
... Alloy UTS ( KSI ) 0.2 % Y.S. ( KSI ) % El Alloy C 120 58 48 Alloy C - 276 110 53 62 Alloy C - 4 116 59 55 Alloy 22 106 52 65 Alloy 59 112 55 65 Within the statistical variation the room temperature mechanical properties of Alloy C - 276 , ...
Page 281
... Alloy C - 276 was superior to Alloy 22 . Figures 2 and 3 show the iso - corrosion curves for Alloy 59 in hydrochloric acid and sulfuric acid . Thermal stability Fig . 4 shows the Time - Temperature - Precipitation ( TTP ) diagram of Alloy ...
... Alloy C - 276 was superior to Alloy 22 . Figures 2 and 3 show the iso - corrosion curves for Alloy 59 in hydrochloric acid and sulfuric acid . Thermal stability Fig . 4 shows the Time - Temperature - Precipitation ( TTP ) diagram of Alloy ...
Contents
Scale Formation During Nucleate Boiling A Review | 26 |
Change in Boiling Mechanism with Time | 33 |
Heat Transfer Models in the Presence of Deposit | 43 |
34 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesion AISI alkali Alloy 59 aluminium anodic anticorrosive application ASTM austenitic bacteria behaviour biocide biofilm biofouling boiling bubble carbon steel cathodic protection cells chemical chloride chromate composition concentration concrete cooling water corrosion inhibitors corrosion rate corrosion resistance cost crevice corrosion current density decrease deposit effect electrochemical electrode Engineering environment erosion evaluation experimental exposure fluid formation fouling growth heat exchangers heat flux heat transfer coefficient heat transfer surface impact inclusions increase industrial ions iron laboratory layer marine materials mechanism metal surface method Michael Schorr NACE nickel nucleation obtained oxide oxygen ozone paint particles passive film phosphate coatings pigment pitting corrosion polarization present Pseudomonas fluorescens rebars reduced samples scale sea water seawater shear slurry solubility solution specimens stainless steel stress corrosion cracking structure Table Technology temperature thermal thickness tube values velocity W/mē weld zinc phosphate