Corrosion Reviews, Volumes 14-15Scientific Publications Division, Freund Publishing House, 1996 |
From inside the book
Results 1-3 of 63
Page 265
... specimens were suspended in sea water that was drawn from the Strait of Juan de Fuca and directed through a tank measuring 16 x 62 x 177 cm . The sea water flowed past any specimen immersed in it at a rate of 1 cm / sec and was then ...
... specimens were suspended in sea water that was drawn from the Strait of Juan de Fuca and directed through a tank measuring 16 x 62 x 177 cm . The sea water flowed past any specimen immersed in it at a rate of 1 cm / sec and was then ...
Page 297
... specimens were introduced , better simulating the natural conditions , and by using Laser Interferometry the interpretation of the formation of active path was obtained . For specimens with notch facing downwards and horizontally ...
... specimens were introduced , better simulating the natural conditions , and by using Laser Interferometry the interpretation of the formation of active path was obtained . For specimens with notch facing downwards and horizontally ...
Page 499
... specimens of type 316L stainless steel were tested in natural flowing seawater . Specimens of approximately 2 cm2 were mounted in epoxy resin and initially mechanically polished to a 120 grit finish with silicon carbide grinding paper ...
... specimens of type 316L stainless steel were tested in natural flowing seawater . Specimens of approximately 2 cm2 were mounted in epoxy resin and initially mechanically polished to a 120 grit finish with silicon carbide grinding paper ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings