Corrosion Reviews, Volumes 14-15Scientific Publications Division, Freund Publishing House, 1996 |
From inside the book
Results 1-3 of 58
Page 128
... showed that it diminishes during the early days of exposure due to the formation of iron compounds which , in turn , originate a protective layer on the steel substrate / 6 / . This behaviour in the corrosion potential was found to ...
... showed that it diminishes during the early days of exposure due to the formation of iron compounds which , in turn , originate a protective layer on the steel substrate / 6 / . This behaviour in the corrosion potential was found to ...
Page 316
... showed intergranular failure too . Finally , in a concentrated solution of 25 % NaCl , where the specimen was immune to stress corrosion cracking , the transients were rarely seen . Instead , this specimen showed a " normal " or white ...
... showed intergranular failure too . Finally , in a concentrated solution of 25 % NaCl , where the specimen was immune to stress corrosion cracking , the transients were rarely seen . Instead , this specimen showed a " normal " or white ...
Page 336
... showed pitting ; at the same time all three types of deposits showed similar corrosion resistance in anodic polarization tests / 29 / . Corrosion potentials and current densities did not necessarily correspond to the salt - spray ...
... showed pitting ; at the same time all three types of deposits showed similar corrosion resistance in anodic polarization tests / 29 / . Corrosion potentials and current densities did not necessarily correspond to the salt - spray ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings