Corrosion Reviews, Volumes 14-15Scientific Publications Division, Freund Publishing House, 1996 |
From inside the book
Results 1-3 of 84
Page 91
... samples 1 , 2 , 8-10 with low thicknesses ( 20-50 μm ) is shown in Fig . 1a . For sample 10 the corrosion potential remains constant throughout the 60 days immersion , while those corresponding to samples 1 , 2 , 8 and 9 tend rapidly to ...
... samples 1 , 2 , 8-10 with low thicknesses ( 20-50 μm ) is shown in Fig . 1a . For sample 10 the corrosion potential remains constant throughout the 60 days immersion , while those corresponding to samples 1 , 2 , 8 and 9 tend rapidly to ...
Page 392
... samples were held in a Teflon holder during the corrosion tests . The holder was designed so that 1 cm2 of the sample surface was exposed to the corrosion media . Two high purity graphite rods were used as the counter electrodes . The ...
... samples were held in a Teflon holder during the corrosion tests . The holder was designed so that 1 cm2 of the sample surface was exposed to the corrosion media . Two high purity graphite rods were used as the counter electrodes . The ...
Page 402
... samples . However , this does not indicate that the bacteria inhibit corrosion . Although the overall corrosion rate of the samples is reduced , heavy localized pitting occurs in the samples exposed to the bacteria . Localized corrosion ...
... samples . However , this does not indicate that the bacteria inhibit corrosion . Although the overall corrosion rate of the samples is reduced , heavy localized pitting occurs in the samples exposed to the bacteria . Localized corrosion ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings