HIGH BUILD ANTIFOULING PAINTS BASED ON DISPROPORTIONATED CALCIUM RESINATE C. A. Giúdice ' and J. C. Benítez ? CIDEPINT : Centro de Investigación y Desarrollo en Tecnologia de Pinturas , ( CIC - CONICET ) .
HIGH BUILD ANTIFOULING PAINTS BASED ON DISPROPORTIONATED CALCIUM RESINATE C. A. Giúdice ' and J. C. Benítez ? CIDEPINT : Centro de Investigación y Desarrollo en Tecnologia de Pinturas , ( CIC - CONICET ) .
Page 2
Disproportionated Calcium Resinate INTRODUCTION New products and raw materials applied to the manufacture of antifouling paints are constantly being researched and developed . One of the advantages of this fact , from a chemical and a ...
Disproportionated Calcium Resinate INTRODUCTION New products and raw materials applied to the manufacture of antifouling paints are constantly being researched and developed . One of the advantages of this fact , from a chemical and a ...
Page 13
Now , toxicant dispersion both in the absence or in the presence of calcium resinate and the time selected for pigment processing do not have a significant influence on the paint bioactivity . However , it markedly simplifies the paint ...
Now , toxicant dispersion both in the absence or in the presence of calcium resinate and the time selected for pigment processing do not have a significant influence on the paint bioactivity . However , it markedly simplifies the paint ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
19 other sections not shown
Other editions - View all
Common terms and phrases
according acid active addition alloys aluminum analysis anodic anticorrosive application behaviour calculated cathodic changes characteristics chemical chloride coatings components composition concentration containing corrosion corrosion rate cracking density depends deposits determined effect electrochemical engineering environment evaluation experimental expert system exposure failure Figure film formation formulation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors interface International iron Italy knowledge layer materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance phosphate pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance salt samples selection showed solution species steel stress structure surface Table techniques Technology temperature tests thickness values zinc