Page 286
... ratio ranges from 2 to 16 along the thickness , being the lowest ratio near the vane surface where MgSO4 is the main compound . However , the Mg / V ratio of these deposits shows a particular feature : in the layer near to the metal ...
... ratio ranges from 2 to 16 along the thickness , being the lowest ratio near the vane surface where MgSO4 is the main compound . However , the Mg / V ratio of these deposits shows a particular feature : in the layer near to the metal ...
Page 449
... ratio in a Mg - Al alloy is considered to be a fairly reliable parameter for an assessment of its corrosion resistance . For a given casting procedure , this ratio correlates with the average Fe / Mn ratio in the intermetallic Al - Mn ...
... ratio in a Mg - Al alloy is considered to be a fairly reliable parameter for an assessment of its corrosion resistance . For a given casting procedure , this ratio correlates with the average Fe / Mn ratio in the intermetallic Al - Mn ...
Page 450
... ratio in particles Correlation between average Fe / Mn ratio in the intermetallic Al- Mn - Fe phases and the corrosion rate ( mg / cm2day1 ) of mould cast alloy AZ91 in 5 % NaCl solution . Particle compositions have been determined by ...
... ratio in particles Correlation between average Fe / Mn ratio in the intermetallic Al- Mn - Fe phases and the corrosion rate ( mg / cm2day1 ) of mould cast alloy AZ91 in 5 % NaCl solution . Particle compositions have been determined by ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings