From inside the book
Results 1-3 of 53
Page 38
LABORATORY TESTS Salt spray ( fog ) testing and 100 % relative humidity chamber SAE 1010 test panels ( 150 x 80 x 2 mm ) were used . The surface ( initial grade A ) was sandblasted to Sa 2 1/2 ( SIS 05 59 00-67 ) attaining 20 um maximum ...
LABORATORY TESTS Salt spray ( fog ) testing and 100 % relative humidity chamber SAE 1010 test panels ( 150 x 80 x 2 mm ) were used . The surface ( initial grade A ) was sandblasted to Sa 2 1/2 ( SIS 05 59 00-67 ) attaining 20 um maximum ...
Page 75
1 : Site of study and location of test panels series ( 1 ) . floating a dock , about 0.3 m to 1.5 m below the water surface to provide the record of macrofouling organisms for four different depths ( Fig.2 ) . Every month one series was ...
1 : Site of study and location of test panels series ( 1 ) . floating a dock , about 0.3 m to 1.5 m below the water surface to provide the record of macrofouling organisms for four different depths ( Fig.2 ) . Every month one series was ...
Page 124
and Zinc Molybdophosphate in Alkyd Paints Table I Pigment formula expressed as % by volume Anticorrosive pigment Talc Titanium dioxide Barite 30.0 29.1 11.8 29.1 The paints were applied by brush on SAE 1010 steel panels ( 15.0x7.5x0.2 ...
and Zinc Molybdophosphate in Alkyd Paints Table I Pigment formula expressed as % by volume Anticorrosive pigment Talc Titanium dioxide Barite 30.0 29.1 11.8 29.1 The paints were applied by brush on SAE 1010 steel panels ( 15.0x7.5x0.2 ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
19 other sections not shown
Other editions - View all
Common terms and phrases
according acid active addition alloys aluminum analysis anodic anticorrosive application behaviour calculated cathodic changes characteristics chemical chloride coatings components composition concentration containing corrosion corrosion rate cracking density depends deposits determined effect electrochemical engineering environment evaluation experimental expert system exposure failure Figure film formation formulation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors interface International iron Italy knowledge layer materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance phosphate pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance salt samples selection showed solution species steel stress structure surface Table techniques Technology temperature tests thickness values zinc