Corrosion Reviews, Volumes 14-15Scientific Publications Division, Freund Publishing House, 1996 |
From inside the book
Results 1-3 of 96
Page 48
... paint viscosity ( generally viscosity loss ) , breaking of the emulsion , changes of pH and the appearance of bacterial ( or fungal ) colonies on the surface where the paint was applied . Any one of these symptoms can lead to ...
... paint viscosity ( generally viscosity loss ) , breaking of the emulsion , changes of pH and the appearance of bacterial ( or fungal ) colonies on the surface where the paint was applied . Any one of these symptoms can lead to ...
Page 64
Electrochemical Properties of Zinc - Ethyl Silicate Paints E , mV vs Ag / AgCl -800 -900 Paint 1 Paint 2 ▽ Paint 3 -1000 -1100 Paint 1 Paint 4 -700 Paint 5 -800 -900 -1000 < -1100 Paint 1 Paint 6 Paint 7 -700 -800 -900 -1000 -1100 10 ...
Electrochemical Properties of Zinc - Ethyl Silicate Paints E , mV vs Ag / AgCl -800 -900 Paint 1 Paint 2 ▽ Paint 3 -1000 -1100 Paint 1 Paint 4 -700 Paint 5 -800 -900 -1000 < -1100 Paint 1 Paint 6 Paint 7 -700 -800 -900 -1000 -1100 10 ...
Page 66
... paint ( Paint 6 ) . When the acid content was higher than that of the reference paint ( Paint 7 ) , bad anticorrosive properties were observed . AC resistance measurements Resistivity did not increase very much for most paints within ...
... paint ( Paint 6 ) . When the acid content was higher than that of the reference paint ( Paint 7 ) , bad anticorrosive properties were observed . AC resistance measurements Resistivity did not increase very much for most paints within ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings