Page 455
As indicated by the same figure , the Al composition attains a constant level after a certain oxide thickness is attained . Moreover , the aluminium concentration in the oxide reaches a terminal level of about 35 atom % independent of ...
As indicated by the same figure , the Al composition attains a constant level after a certain oxide thickness is attained . Moreover , the aluminium concentration in the oxide reaches a terminal level of about 35 atom % independent of ...
Page 473
Thickness increases with temperature ; typically 10 nm after heat treatment at 400 ° C . In contrast with humid environments , the external side of the oxide film hydrolyses to produce hydrated oxides such as bayerite ( Al2O3 , 3H2O or ...
Thickness increases with temperature ; typically 10 nm after heat treatment at 400 ° C . In contrast with humid environments , the external side of the oxide film hydrolyses to produce hydrated oxides such as bayerite ( Al2O3 , 3H2O or ...
Page 474
Within the aluminium oxide film , O " anion and Al3 + cation are both mobile ; their transport numbers are nearly 0.5 so the aluminium oxide film simultaneously grows at both interfaces / 5 / . This oxide formation process produces an ...
Within the aluminium oxide film , O " anion and Al3 + cation are both mobile ; their transport numbers are nearly 0.5 so the aluminium oxide film simultaneously grows at both interfaces / 5 / . This oxide formation process produces an ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminum analysis anodic application behaviour cathodic cause changes characteristics chemical chloride coatings composition concentration containing corrosion rate corrosion resistance cracking curves density depends deposits determined dissolution effect electrochemical engineering environment evaluation experimental expert system exposure factors failure Figure film formation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors initiation interface International iron Italy knowledge layer limited materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance samples selection showed shown solution specific specimens steel stress structure surface Table techniques Technology temperature tests thickness values zinc