Page 455
... oxide thickness is attained . Moreover , the aluminium concentration in the oxide reaches a terminal level of about 35 atom % independent of the aluminium content of the alloy as long as the latter is equal to or larger than about 4 ...
... oxide thickness is attained . Moreover , the aluminium concentration in the oxide reaches a terminal level of about 35 atom % independent of the aluminium content of the alloy as long as the latter is equal to or larger than about 4 ...
Page 473
... oxide film hydrolyses to produce hydrated oxides such as bayerite ( Al2O3 , 3H2O or Al ( OH ) 2 ) formed under 70 ° C and bohmite ( Al2O3 , H2O or AIOOH ) formed above 100 ° C / 2 / . Because hydrated oxides are less protective than ...
... oxide film hydrolyses to produce hydrated oxides such as bayerite ( Al2O3 , 3H2O or Al ( OH ) 2 ) formed under 70 ° C and bohmite ( Al2O3 , H2O or AIOOH ) formed above 100 ° C / 2 / . Because hydrated oxides are less protective than ...
Page 474
... oxide film simultaneously grows at both interfaces / 5 / . This oxide formation process produces an oxide film that is very adhesive to the aluminium metal ( no voids are produced between metal and oxide , during oxide formation ) . In ...
... oxide film simultaneously grows at both interfaces / 5 / . This oxide formation process produces an oxide film that is very adhesive to the aluminium metal ( no voids are produced between metal and oxide , during oxide formation ) . In ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings