... observed in 20 % NaCl , pH 3 , and they became anodic this time . This specimen did fail by stress corrosion cracking and showed intergranular failure too . Finally , in a concentrated solution of 25 % NaCl , where the specimen was ...
... observed in 20 % NaCl , pH 3 , and they became anodic this time . This specimen did fail by stress corrosion cracking and showed intergranular failure too . Finally , in a concentrated solution of 25 % NaCl , where the specimen was ...
Page 319
... observed , which means that the specimen is undergoing uniform corrosion / 17 / . The transients observed in this case are probably due to the exposure of fresh metal to the environment once necking has initiated allowing anodic ...
... observed , which means that the specimen is undergoing uniform corrosion / 17 / . The transients observed in this case are probably due to the exposure of fresh metal to the environment once necking has initiated allowing anodic ...
Page 397
... observed to occur in patches over the entire sample surface , Figure 10 . Corrosion of the composite sample in the pure media was also observed to be localized to certain regions , as seen in Figure 11. Local pits were observed to form ...
... observed to occur in patches over the entire sample surface , Figure 10 . Corrosion of the composite sample in the pure media was also observed to be localized to certain regions , as seen in Figure 11. Local pits were observed to form ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings