Page 316
When a concentration of 15 % NaCl was reached , the transients were similar in both , intensity and frequency , than those observed in 20 % NaCl , pH 3 , and they became anodic this time . This specimen did fail by stress corrosion ...
When a concentration of 15 % NaCl was reached , the transients were similar in both , intensity and frequency , than those observed in 20 % NaCl , pH 3 , and they became anodic this time . This specimen did fail by stress corrosion ...
Page 319
6 ) a white noise pattern , which consisted of random signal fluctuations , was observed , which means that the specimen is undergoing uniform corrosion / 17 / . The transients observed in this case are probably due to the exposure of ...
6 ) a white noise pattern , which consisted of random signal fluctuations , was observed , which means that the specimen is undergoing uniform corrosion / 17 / . The transients observed in this case are probably due to the exposure of ...
Page 397
Scanning electron microscopy of the surfaces of the corroded samples was carried out in order to explain part of the observed behavior . The unreinforced alloy formed a uniform layer of corrosion product ( Al2O3 ) on its surface ...
Scanning electron microscopy of the surfaces of the corroded samples was carried out in order to explain part of the observed behavior . The unreinforced alloy formed a uniform layer of corrosion product ( Al2O3 ) on its surface ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminum analysis anodic application behaviour cathodic cause changes characteristics chemical chloride coatings composition concentration containing corrosion rate corrosion resistance cracking curves density depends deposits determined dissolution effect electrochemical engineering environment evaluation experimental expert system exposure factors failure Figure film formation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors initiation interface International iron Italy knowledge layer limited materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance samples selection showed shown solution specific specimens steel stress structure surface Table techniques Technology temperature tests thickness values zinc