Page 310
However, the use of electrochemical noise for the study of stress corrosion cracking has been limited. Newman /10/ used the random fluctuations in current during the transgranular stress corrosion cracking of a-brass in sodium nitrite ...
However, the use of electrochemical noise for the study of stress corrosion cracking has been limited. Newman /10/ used the random fluctuations in current during the transgranular stress corrosion cracking of a-brass in sodium nitrite ...
Page 360
It was therefore concluded that the SCC process in pure titanium was governed by a mass transport reaction limited by either molecular species of the type X2 or ionic species of the type X " ( X = Cl , Br or I ) in solution , this in ...
It was therefore concluded that the SCC process in pure titanium was governed by a mass transport reaction limited by either molecular species of the type X2 or ionic species of the type X " ( X = Cl , Br or I ) in solution , this in ...
Page 371
The polarization curves in Figure 5 also demonstrate that the galvanic - corrosion rate is highly dependent on the kinetics of oxygen reduction as either limited by activation or oxygen diffusion . For reinforcements of very high ...
The polarization curves in Figure 5 also demonstrate that the galvanic - corrosion rate is highly dependent on the kinetics of oxygen reduction as either limited by activation or oxygen diffusion . For reinforcements of very high ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminum analysis anodic application behaviour cathodic cause changes characteristics chemical chloride coatings composition concentration containing corrosion rate corrosion resistance cracking curves density depends deposits determined dissolution effect electrochemical engineering environment evaluation experimental expert system exposure factors failure Figure film formation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors initiation interface International iron Italy knowledge layer limited materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance samples selection showed shown solution specific specimens steel stress structure surface Table techniques Technology temperature tests thickness values zinc