Page 450
... limit . For AZ91 this Fe / Mn ratio has been determined to be about 0.032 / 18 / . However , based on extensive corrosion tests on a large number of specimens exhibiting Fe and Mn concentrations covering a wide range , the relevance of ...
... limit . For AZ91 this Fe / Mn ratio has been determined to be about 0.032 / 18 / . However , based on extensive corrosion tests on a large number of specimens exhibiting Fe and Mn concentrations covering a wide range , the relevance of ...
Page 458
... limits further oxidation of the film resulting in improved corrosion resistance . Thus , both XPS and TEM studies ... limit at about this threshold to form a continuous passivating network . EFFECT OF OTHER ALLOYING ELEMENTS Zinc It ...
... limits further oxidation of the film resulting in improved corrosion resistance . Thus , both XPS and TEM studies ... limit at about this threshold to form a continuous passivating network . EFFECT OF OTHER ALLOYING ELEMENTS Zinc It ...
Page 480
... limit Cl ̄ build up and acidification within pits , and help homogenisation of the pit solution with the bulk ... limits the oxychloride dissolution , which controls pitting corrosion . For Szlarska- Smialowska / 42 / migration within ...
... limit Cl ̄ build up and acidification within pits , and help homogenisation of the pit solution with the bulk ... limits the oxychloride dissolution , which controls pitting corrosion . For Szlarska- Smialowska / 42 / migration within ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings