Page 255
The sediment consisted of two layers of the same approximate thickness . The external layer contained sodium sulfate ( Na2SO4 ) and sodium vanadate ( Na3VO3 ) , in relative concentrations of about 6.4 : 1 . This layer had a porous ...
The sediment consisted of two layers of the same approximate thickness . The external layer contained sodium sulfate ( Na2SO4 ) and sodium vanadate ( Na3VO3 ) , in relative concentrations of about 6.4 : 1 . This layer had a porous ...
Page 286
Magnesium vanadates are present in all along the deposit , but its concentration is higher in the outer layer . ... were analyzed in order to find the main differences among the several layers constituting the deposit .
Magnesium vanadates are present in all along the deposit , but its concentration is higher in the outer layer . ... were analyzed in order to find the main differences among the several layers constituting the deposit .
Page 176
An artificial neural network may also consist of layers of interconnected neurons . A network is composed of one output layer , one input layer , and any number of hidden layers ( no more than three are necessary ) .
An artificial neural network may also consist of layers of interconnected neurons . A network is composed of one output layer , one input layer , and any number of hidden layers ( no more than three are necessary ) .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminum analysis anodic application behaviour cathodic cause changes characteristics chemical chloride coatings composition concentration containing corrosion rate corrosion resistance cracking curves density depends deposits determined dissolution effect electrochemical engineering environment evaluation experimental expert system exposure factors failure Figure film formation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors initiation interface International iron Italy knowledge layer limited materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance samples selection showed shown solution specific specimens steel stress structure surface Table techniques Technology temperature tests thickness values zinc