Page 283
... deposits built during operation with the 260 ppm V fuel oil than for the friable deposits formed with the 130 ppm V fuel oil . In contrast , the Mg / SO , ratio exhibits the opposite trend . It also can be seen the similar Mg / V values ...
... deposits built during operation with the 260 ppm V fuel oil than for the friable deposits formed with the 130 ppm V fuel oil . In contrast , the Mg / SO , ratio exhibits the opposite trend . It also can be seen the similar Mg / V values ...
Page 284
... deposit thickness reached 13.4 mm ; with Epsom salt , 15 mm thick deposits were observed . Structure of Ash Deposits X - ray diffraction analysis indicated that the major phases present in the ash deposits are MgSO4 , MgO and Mg3V2Og ...
... deposit thickness reached 13.4 mm ; with Epsom salt , 15 mm thick deposits were observed . Structure of Ash Deposits X - ray diffraction analysis indicated that the major phases present in the ash deposits are MgSO4 , MgO and Mg3V2Og ...
Page 291
... deposit formation . Urbas and Tomlinson / 23,24 / reported a change in the consistency of the deposits from soft to hard in a simulated gas turbine combustor operating at a pressure of 5 atmospheres with 1 to 2 wt . % S in the fuel ...
... deposit formation . Urbas and Tomlinson / 23,24 / reported a change in the consistency of the deposits from soft to hard in a simulated gas turbine combustor operating at a pressure of 5 atmospheres with 1 to 2 wt . % S in the fuel ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings