Corrosion Reviews, Volumes 14-15Scientific Publications Division, Freund Publishing House, 1996 |
From inside the book
Results 1-3 of 91
Page 310
... cracking has been limited . Newman / 10 / used the random fluctuations in current during the transgranular stress corrosion cracking of a - brass in sodium nitrite to demonstrate the discontinuous nature of cracking in this system ...
... cracking has been limited . Newman / 10 / used the random fluctuations in current during the transgranular stress corrosion cracking of a - brass in sodium nitrite to demonstrate the discontinuous nature of cracking in this system ...
Page 316
... cracking , i.e. a few tens of milivolts ; however , this specimen was immune to stress corrosion cracking , and showed only ductile type of failure with microvoid coalescence and plastic deformation . In 20 % Na2SO4 , in the elastic ...
... cracking , i.e. a few tens of milivolts ; however , this specimen was immune to stress corrosion cracking , and showed only ductile type of failure with microvoid coalescence and plastic deformation . In 20 % Na2SO4 , in the elastic ...
Page 100
... cracking and anodic stress corrosion cracking are of particular concern when selecting CRA materials . Further , for many CRAS there is relatively limited documented field experi- ence to define their limits of use . Selection of CRAS ...
... cracking and anodic stress corrosion cracking are of particular concern when selecting CRA materials . Further , for many CRAS there is relatively limited documented field experi- ence to define their limits of use . Selection of CRAS ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings