Corrosion Reviews, Volumes 14-15Scientific Publications Division, Freund Publishing House, 1996 |
From inside the book
Results 1-3 of 81
Page 17
... coatings are accepted as behaving like porous electrodes due to the presence of voids . Electrochemical impedance spectroscopy has previously been applied to study the protective behaviour of these coatings / 19-21,27-29 / , but until ...
... coatings are accepted as behaving like porous electrodes due to the presence of voids . Electrochemical impedance spectroscopy has previously been applied to study the protective behaviour of these coatings / 19-21,27-29 / , but until ...
Page 359
... coatings . • Knowledge of modeling of degradation processes will enable prediction of coating lifetime . UV ... coatings system . REFERENCES 1. Athey , Robert D. " Testing coatings : An overview " , Metal Finishing , 92 ( 5A ) , 298-346 ...
... coatings . • Knowledge of modeling of degradation processes will enable prediction of coating lifetime . UV ... coatings system . REFERENCES 1. Athey , Robert D. " Testing coatings : An overview " , Metal Finishing , 92 ( 5A ) , 298-346 ...
Page 360
... coatings by the use of pigmented polymer beads " , J. of Coatings Technology , 54 ( 695 ) , 19-24 ( 1982 ) . 16. Hegedus , C.R. and Kamel , I.L. “ Thermodynamic analysis of pigment and polymer surfaces using inverse gas chromatography ...
... coatings by the use of pigmented polymer beads " , J. of Coatings Technology , 54 ( 695 ) , 19-24 ( 1982 ) . 16. Hegedus , C.R. and Kamel , I.L. “ Thermodynamic analysis of pigment and polymer surfaces using inverse gas chromatography ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings