Page 305
Atmospheric tower over head chloride content versus magnesium content in crude after desalter 0 CO atmosphorts tower over head chloride content as ppm CI 20 10 0 0.03 0.05 0.07 0.09 0.11 0.13 magnesium content in crude or doctor a ppon ...
Atmospheric tower over head chloride content versus magnesium content in crude after desalter 0 CO atmosphorts tower over head chloride content as ppm CI 20 10 0 0.03 0.05 0.07 0.09 0.11 0.13 magnesium content in crude or doctor a ppon ...
Page 348
It should also be mentioned that the threshold stress for some titanium alloys , notably Ti - 6A1-4V / 18 / , Ti - 5Al - 2.5Sn / 201 , Ti - 13V - 11Cr - 3A1 / 21 / and Ti - 155 / 19 / when measured in aqueous chloride environments , is ...
It should also be mentioned that the threshold stress for some titanium alloys , notably Ti - 6A1-4V / 18 / , Ti - 5Al - 2.5Sn / 201 , Ti - 13V - 11Cr - 3A1 / 21 / and Ti - 155 / 19 / when measured in aqueous chloride environments , is ...
Page 391
However , in contrast to Fischer and Heusler , a passivity breakdown in the absence of chloride ions for iron metal has been proposed by Löcher and Strehblow / 121 / through their split - ring experiments . They predicted the exposure ...
However , in contrast to Fischer and Heusler , a passivity breakdown in the absence of chloride ions for iron metal has been proposed by Löcher and Strehblow / 121 / through their split - ring experiments . They predicted the exposure ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
19 other sections not shown
Other editions - View all
Common terms and phrases
according acid active addition alloys aluminum analysis anodic anticorrosive application behaviour calculated cathodic changes characteristics chemical chloride coatings components composition concentration containing corrosion corrosion rate cracking density depends deposits determined effect electrochemical engineering environment evaluation experimental expert system exposure failure Figure film formation formulation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors interface International iron Italy knowledge layer materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance phosphate pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance salt samples selection showed solution species steel stress structure surface Table techniques Technology temperature tests thickness values zinc