... alloys increased with P content ; alloys with 11.8 , 13.6 and 15.0 wt % P were characterized by 1.1 , 1.9 , 2.6 % of elongation respectively / 55 / . According to Zeller and Landau ( 1991 ) / 29 / , the elongation of NiP alloys with ...
... alloys increased with P content ; alloys with 11.8 , 13.6 and 15.0 wt % P were characterized by 1.1 , 1.9 , 2.6 % of elongation respectively / 55 / . According to Zeller and Landau ( 1991 ) / 29 / , the elongation of NiP alloys with ...
Page 337
... alloys shifted in the negative range / 48,34 / . In the last cases the crystallization processes were probably predominant . CONCLUSIONS 1. NiP alloys containing up to 17 wt % P can be electrodeposited with current efficiency 10-80 ...
... alloys shifted in the negative range / 48,34 / . In the last cases the crystallization processes were probably predominant . CONCLUSIONS 1. NiP alloys containing up to 17 wt % P can be electrodeposited with current efficiency 10-80 ...
Page 427
... alloys with a greater lithium concentration are characterized by lower passivating ability ( Fig . 2c , d ) than the alloys with a lower content of this component . At the same time , with the increase of lithium concentration to 2.3 ...
... alloys with a greater lithium concentration are characterized by lower passivating ability ( Fig . 2c , d ) than the alloys with a lower content of this component . At the same time , with the increase of lithium concentration to 2.3 ...
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid alloys aluminum analysis anodic anticorrosive application aqueous ASTM behaviour binder Biofouling calcium resinate carbon cathodic protection Chem chemical chloride CO₂ composition concentration containing corrosion control corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance Corrosion Reviews current density deposits dissolution effect electrochemical electrode electrolyte engineering environment epoxy evaluation experimental expert system exposure film thickness fuel function galvanic corrosion gas turbine hydrogen immersion impedance increase industry inhibition inhibitors interface layer materials measurements mechanism metal Michael Schorr NACE NACE International oxide paint film panels parameters particles performance petrochemical pigment pitting corrosion polarization curves polymer potentiostatic prediction present properties reaction samples silicate Skoulikidis sodium solution specific specimens steel stress corrosion cracking structure substrate surface system developer Table techniques Technology temperature tests titanium values WW rosin zinc ZRP coatings