Page 335
The internal stress in NiP alloys was reduced on addition of a stress - relaxing agent , such as saccharin , Na saccharin , p - toluenesulfonamide and / or Na benzenesulfonate / 1,19,22 / . These agents changed the tensile stress of 290 ...
The internal stress in NiP alloys was reduced on addition of a stress - relaxing agent , such as saccharin , Na saccharin , p - toluenesulfonamide and / or Na benzenesulfonate / 1,19,22 / . These agents changed the tensile stress of 290 ...
Page 337
The effect of the heat treatment on the corrosion resistance of NiP alloys and NiP composites is determined by ordering of the coating structure , and by reduction of the defect concentration and of the internal stress .
The effect of the heat treatment on the corrosion resistance of NiP alloys and NiP composites is determined by ordering of the coating structure , and by reduction of the defect concentration and of the internal stress .
Page 427
However , the value of current density in the passive region for Al - 2.3 % Li alloy exceeds the indicated parameter by a factor of 15 as ... although in the first method of plotting the curve this value is identical for both alloys .
However , the value of current density in the passive region for Al - 2.3 % Li alloy exceeds the indicated parameter by a factor of 15 as ... although in the first method of plotting the curve this value is identical for both alloys .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminum analysis anodic application behaviour cathodic cause changes characteristics chemical chloride coatings composition concentration containing corrosion rate corrosion resistance cracking curves density depends deposits determined dissolution effect electrochemical engineering environment evaluation experimental expert system exposure factors failure Figure film formation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors initiation interface International iron Italy knowledge layer limited materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance samples selection showed shown solution specific specimens steel stress structure surface Table techniques Technology temperature tests thickness values zinc