Addition of other anions , for example SO ?, OH " , NO3- , PO2 and Cro2 either had no effect or acted as inhibitors / 10,41,447 . The addition of some cations can also affect the stress corrosion behaviour of some alloys / 10,41,45,461 ...
Addition of other anions , for example SO ?, OH " , NO3- , PO2 and Cro2 either had no effect or acted as inhibitors / 10,41,447 . The addition of some cations can also affect the stress corrosion behaviour of some alloys / 10,41,45,461 ...
Page 359
They also showed that in alloys containing high Al failures could be prevented through inhibition of the initiation process by cathodic polarisation or the introduction of passivators , for example , the addition of water to the ...
They also showed that in alloys containing high Al failures could be prevented through inhibition of the initiation process by cathodic polarisation or the introduction of passivators , for example , the addition of water to the ...
Page 363
Stage I H ++ M + e * = Hed Had = Hab ( 10 ) ( 11 ) Stage 2HQd = H2 ( gas ) ( 12 ) Adepoju / 19 / and later Lycett / 797 related the effect of Pt , Hg , Sn and As cation additions on either the absorption ( reaction 11 ) or the ...
Stage I H ++ M + e * = Hed Had = Hab ( 10 ) ( 11 ) Stage 2HQd = H2 ( gas ) ( 12 ) Adepoju / 19 / and later Lycett / 797 related the effect of Pt , Hg , Sn and As cation additions on either the absorption ( reaction 11 ) or the ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
19 other sections not shown
Other editions - View all
Common terms and phrases
according acid active addition alloys aluminum analysis anodic anticorrosive application behaviour calculated cathodic changes characteristics chemical chloride coatings components composition concentration containing corrosion corrosion rate cracking density depends deposits determined effect electrochemical engineering environment evaluation experimental expert system exposure failure Figure film formation formulation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors interface International iron Italy knowledge layer materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance phosphate pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance salt samples selection showed solution species steel stress structure surface Table techniques Technology temperature tests thickness values zinc