Page 351
Several workers / 10,41-43 / have investigated the effect of halide additions to distilled water . ... Addition of other anions , for example SO12 , OH , NO3 " , PO43 and CrO42 either had no effect or acted as inhibitors / 10,41,44 / .
Several workers / 10,41-43 / have investigated the effect of halide additions to distilled water . ... Addition of other anions , for example SO12 , OH , NO3 " , PO43 and CrO42 either had no effect or acted as inhibitors / 10,41,44 / .
Page 359
They also showed that in alloys containing high Al failures could be prevented through inhibition of the initiation process by cathodic polarisation or the introduction of passivators , for example , the addition of water to the ...
They also showed that in alloys containing high Al failures could be prevented through inhibition of the initiation process by cathodic polarisation or the introduction of passivators , for example , the addition of water to the ...
Page 363
Stage I H ++ M + e = Had Had = Hab Stage II 2Had = H2 ( gas ) ( 10 ) ( 11 ) ( 12 ) Adepoju / 19 / and later Lycett / 79 / related the effect of Pt , Hg , Sn and As cation additions on either the absorption ( reaction 11 ) or the ...
Stage I H ++ M + e = Had Had = Hab Stage II 2Had = H2 ( gas ) ( 10 ) ( 11 ) ( 12 ) Adepoju / 19 / and later Lycett / 79 / related the effect of Pt , Hg , Sn and As cation additions on either the absorption ( reaction 11 ) or the ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
22 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminum analysis anodic application behaviour cathodic cause changes characteristics chemical chloride coatings composition concentration containing corrosion rate corrosion resistance cracking curves density depends deposits determined dissolution effect electrochemical engineering environment evaluation experimental expert system exposure factors failure Figure film formation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors initiation interface International iron Italy knowledge layer limited materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance samples selection showed shown solution specific specimens steel stress structure surface Table techniques Technology temperature tests thickness values zinc