Page 17
Thus , an interpretation of the changes in the impedance spectrum , accounting for the variations in the zinc active area of the electrode was also lacking The physico - chemical properties of ZRP are affected by the content of zinc in ...
Thus , an interpretation of the changes in the impedance spectrum , accounting for the variations in the zinc active area of the electrode was also lacking The physico - chemical properties of ZRP are affected by the content of zinc in ...
Page 25
The decrease of the capacitance as well as the increase of the resistance Ra can be attributed to a progressive decrease of the electrochemically active area of active zinc due to the accumulation of corrosion products in the porous ...
The decrease of the capacitance as well as the increase of the resistance Ra can be attributed to a progressive decrease of the electrochemically active area of active zinc due to the accumulation of corrosion products in the porous ...
Page 381
Low - Integrity Diffusion Bonds Sedriks , Green and Novak / 38 / and Bakulin , Ivanov and Kuchkin / 39 / found that open - circuit potentials of B / Al MMCs were active to that of their monolithic matrix alloys in aerated NaCl solutions ...
Low - Integrity Diffusion Bonds Sedriks , Green and Novak / 38 / and Bakulin , Ivanov and Kuchkin / 39 / found that open - circuit potentials of B / Al MMCs were active to that of their monolithic matrix alloys in aerated NaCl solutions ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Expert Systems for Corrosion Prevention and Control | 1 |
Use of Computerized Techniques in Corrosion | 15 |
Design and Structure of Knowledge Based Systems | 71 |
19 other sections not shown
Other editions - View all
Common terms and phrases
according acid active addition alloys aluminum analysis anodic anticorrosive application behaviour calculated cathodic changes characteristics chemical chloride coatings components composition concentration containing corrosion corrosion rate cracking density depends deposits determined effect electrochemical engineering environment evaluation experimental expert system exposure failure Figure film formation formulation fuel function higher hydrogen impedance important increase indicated industry inhibition inhibitors interface International iron Italy knowledge layer materials measurements mechanism metal method observed obtained occur operation organic oxide paint panels parameters particles performance phosphate pigment pitting plant polarization potential prediction present problems properties protection reaction reference resinate resistance salt samples selection showed solution species steel stress structure surface Table techniques Technology temperature tests thickness values zinc