... welded components . It has been observed that alloy G heat exchanger tubes suffered corrosive attack at the weld ( Figure 2 ) . Accelerated laboratory tests on as - welded samples confirmed the better corrosion resistance of G - 30 ...
... welded components . It has been observed that alloy G heat exchanger tubes suffered corrosive attack at the weld ( Figure 2 ) . Accelerated laboratory tests on as - welded samples confirmed the better corrosion resistance of G - 30 ...
Page 93
... welded joints in SAF 2507 Procedure 1 : GTAW ( TIG ) of 25 x 1.65 mm tube Procedure 2 : GTAW ( TIG ) of 88.9 x 3.0 ... welded joint is performance tested in respect of mechanical and corrosion properties . This can be seen in several ...
... welded joints in SAF 2507 Procedure 1 : GTAW ( TIG ) of 25 x 1.65 mm tube Procedure 2 : GTAW ( TIG ) of 88.9 x 3.0 ... welded joint is performance tested in respect of mechanical and corrosion properties . This can be seen in several ...
Page 97
... Weld metal 58 39 0.91 0.47 50 % weld / 83 56 1.21 0.75 50 % HAZ Fusion line 118 71 1.45 0.89 Bend testing V - groove ... welded ( manually steel brushed ) : 55 ° C Other Ferrite content : Top layer : 38 % Reheated layer : 31 % Average of ...
... Weld metal 58 39 0.91 0.47 50 % weld / 83 56 1.21 0.75 50 % HAZ Fusion line 118 71 1.45 0.89 Bend testing V - groove ... welded ( manually steel brushed ) : 55 ° C Other Ferrite content : Top layer : 38 % Reheated layer : 31 % Average of ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints