Page 227
The Effect of Coating Thickness From the very earliest studies on porosity onwards , it has been shown that an increase in coating thickness will reduce the porosity / 39,40 / . This phenomenon can be plotted graphically ( Figure 5 ) ...
The Effect of Coating Thickness From the very earliest studies on porosity onwards , it has been shown that an increase in coating thickness will reduce the porosity / 39,40 / . This phenomenon can be plotted graphically ( Figure 5 ) ...
Page 228
6 : Porosity versus thickness for deposits of various preferred crystal orientations / 43 / . With certain electrolytes , Morrissey / 44 / found a three stage porosity / thickness relationship ( Figure 7 ) . These deposits showed no ...
6 : Porosity versus thickness for deposits of various preferred crystal orientations / 43 / . With certain electrolytes , Morrissey / 44 / found a three stage porosity / thickness relationship ( Figure 7 ) . These deposits showed no ...
Page 5
This average volume divided by the surface area ( of the tube say ) gives the biofilm thickness . An electrical conductivity method was developed to measure point values of biofilm thickness / 6 / . Several values of thickness need to ...
This average volume divided by the surface area ( of the tube say ) gives the biofilm thickness . An electrical conductivity method was developed to measure point values of biofilm thickness / 6 / . Several values of thickness need to ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
ELECTROCHEMICAL TECHNIQUES SIMPLE TESTS | 32 |
Electrochemical Techniques Simple Tests for Complex | 34 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloy anodes application behaviour biofilm carbon cathodic cause changes chemical chromate chromium coating complex concentration containing copper corrosion rate curves decrease dependent deposition determination developed edition effect electrochemical electrode engineering equipment evaluation example experimental experiments exposed Figure flow formation fouling frequency function growth heat flux heat transfer higher important included increase industrial inhibition inhibitors installations International ions iron oxide laboratory laser layer low alloy steel materials measurements mechanism metal method observed obtained operating organic paints particles passive performed plant polarization pores porosity possible potential practical prediction present problems protection published range reduce reference removal resistance Science selection shown shows solution specimen stainless steel substrate surface Table techniques Technology temperature thickness treatment volume zinc