Page 238
... test . In some instances , however , the authors of a test have claimed that repeated testing , which induced more pores , was a more accurate and hence recommended procedure / 15,66 / ! 5. PORE DETECTION TESTS Pore detection tests are ...
... test . In some instances , however , the authors of a test have claimed that repeated testing , which induced more pores , was a more accurate and hence recommended procedure / 15,66 / ! 5. PORE DETECTION TESTS Pore detection tests are ...
Page 239
5.2 . Ferricyanide - type Tests The earliest practical porosity tests were methods of this type . A ferricyanide based solution , originally used to test local corrosion behaviour on iron and steel , was suggested as ... Tests Hot Water Test.
5.2 . Ferricyanide - type Tests The earliest practical porosity tests were methods of this type . A ferricyanide based solution , originally used to test local corrosion behaviour on iron and steel , was suggested as ... Tests Hot Water Test.
Page 245
... tests such as the salt spray test / 100 / have sometimes been proposed as porosity tests . It has been shown , however , that salt spray tests should be defined as corrosion tests as they attack many coatings as well as the substrate ...
... tests such as the salt spray test / 100 / have sometimes been proposed as porosity tests . It has been shown , however , that salt spray tests should be defined as corrosion tests as they attack many coatings as well as the substrate ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/mē zinc zinc powder zinc-ethyl silicate paints