Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 74
Page 157
... Temperature Although a large amount of work has been done for the past two decades , on corrosion inhibition by chromates , yet the effect of temperature on the growth and nature of the oxide film has not attracted the attention of ...
... Temperature Although a large amount of work has been done for the past two decades , on corrosion inhibition by chromates , yet the effect of temperature on the growth and nature of the oxide film has not attracted the attention of ...
Page 51
... temperature can be attributed to the change in corrosion kinetics . Data on anodic polarisation curves indicate that if the temperature changes from room temperature to 90 ° C in 1N sulphuric acid the critical anodic current density ic ...
... temperature can be attributed to the change in corrosion kinetics . Data on anodic polarisation curves indicate that if the temperature changes from room temperature to 90 ° C in 1N sulphuric acid the critical anodic current density ic ...
Page 52
... temperature will influence the corrosion rate but may not be much greater . In contrast to the phenomenon that corrosion rates increase with increasing temperature , it is observed that the corrosion rate of alloy 25Cr22Ni2Mo decreases ...
... temperature will influence the corrosion rate but may not be much greater . In contrast to the phenomenon that corrosion rates increase with increasing temperature , it is observed that the corrosion rate of alloy 25Cr22Ni2Mo decreases ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints