Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 76
Page 298
... specimens were irradiated under identical conditions ( 100 W , 40 cm / sec ) by five series of six beam passes with specimen shift between passes being 100 , 200 , 300 , 400 , and 450 μm . For corrosion resistance tests we used specimens ...
... specimens were irradiated under identical conditions ( 100 W , 40 cm / sec ) by five series of six beam passes with specimen shift between passes being 100 , 200 , 300 , 400 , and 450 μm . For corrosion resistance tests we used specimens ...
Page 301
... specimens having painted chromium coating . The Auger spectrum taken from the melt zone of a carbon coated specimen after surface sputtering shows that the height of carbon peak in this specimen is similar to that observed in chromium ...
... specimens having painted chromium coating . The Auger spectrum taken from the melt zone of a carbon coated specimen after surface sputtering shows that the height of carbon peak in this specimen is similar to that observed in chromium ...
Page 326
... specimens which were treated under similar conditions and had approximately the same content of alloying elements in the surface layer behaved quite differently during the potentiodynamic test , with one specimen not showing passivation ...
... specimens which were treated under similar conditions and had approximately the same content of alloying elements in the surface layer behaved quite differently during the potentiodynamic test , with one specimen not showing passivation ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints