Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 53
Page 9
... samples of selected alloys may be tested . Unwelded samples are one - inch square with a 120 - grit ground finish . The welded samples are two inches by one inch and the surfaces are vapor blasted . Duplicate samples are tested . The ...
... samples of selected alloys may be tested . Unwelded samples are one - inch square with a 120 - grit ground finish . The welded samples are two inches by one inch and the surfaces are vapor blasted . Duplicate samples are tested . The ...
Page 261
... sample where the precipitate formed , an I.E.V. at least an order of magnitude larger would be recorded , which was proportional to the number of precipitate sites on the sample . It was not possible to compare sensibly results from samples ...
... sample where the precipitate formed , an I.E.V. at least an order of magnitude larger would be recorded , which was proportional to the number of precipitate sites on the sample . It was not possible to compare sensibly results from samples ...
Page 91
... samples were exposed for 3 months to 1-2 mg Cl2 / 1 chlorinated seawater at temperatures from 30 - 45 ° C . Crevice corrosion samples were tested at 45 ° C . Only one sample of SAF 2507 was slightly attacked ( depth 0.03 mm ) whilst all ...
... samples were exposed for 3 months to 1-2 mg Cl2 / 1 chlorinated seawater at temperatures from 30 - 45 ° C . Crevice corrosion samples were tested at 45 ° C . Only one sample of SAF 2507 was slightly attacked ( depth 0.03 mm ) whilst all ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints