Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 15
Page 85
... runs on an APPLE II computer and drives the Solartron computerized system consisting of a MOD 1286 electrochemical interface and a MOD 1250 frequency response analyzer . Measurements are performed in the galvanostatic configuration so ...
... runs on an APPLE II computer and drives the Solartron computerized system consisting of a MOD 1286 electrochemical interface and a MOD 1250 frequency response analyzer . Measurements are performed in the galvanostatic configuration so ...
Page 86
... of biofilm formation was not always confirmed in the experiments made by the other authors . Oliveira et al.49 carried out several runs with mixed kaolin 86 Vol . 11 , Nos . 1-2 , 1993 Surface Interactions and Deposit.
... of biofilm formation was not always confirmed in the experiments made by the other authors . Oliveira et al.49 carried out several runs with mixed kaolin 86 Vol . 11 , Nos . 1-2 , 1993 Surface Interactions and Deposit.
Page 87
Oliveira et al.49 carried out several runs with mixed kaolin - bacteria suspensions ( 6 x 107 bacteria / ml and 150 mg of kaolin / 1 ) . The experimental procedure was similar to the one mentioned in section 4.2 , except for the fact ...
Oliveira et al.49 carried out several runs with mixed kaolin - bacteria suspensions ( 6 x 107 bacteria / ml and 150 mg of kaolin / 1 ) . The experimental procedure was similar to the one mentioned in section 4.2 , except for the fact ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints