Page 349
... recommended practice for topcoating is to employ a 60-90 μm thick inorganic zinc coating with a high - build epoxy polyamide topcoat , 100-150 μm thickness . Recently it was suggested that a 35-50 μm thick urethane - acrylic coating can ...
... recommended practice for topcoating is to employ a 60-90 μm thick inorganic zinc coating with a high - build epoxy polyamide topcoat , 100-150 μm thickness . Recently it was suggested that a 35-50 μm thick urethane - acrylic coating can ...
Page 379
... recommended for the fabrication of phosphoric acid production equipment , e.g. , Sanicro 28 , ex - Sandvik , Sweden ... recommend expanding Chapter 10 on Corrosion to include the following additions : 1. In the last few years many ...
... recommended for the fabrication of phosphoric acid production equipment , e.g. , Sanicro 28 , ex - Sandvik , Sweden ... recommend expanding Chapter 10 on Corrosion to include the following additions : 1. In the last few years many ...
Page 382
... recommended to provide readers with the tools to deal with diverse problems of analysis and prevention . However , the essential elements of electrochemical corrosion are presented in Chapter 1 , and the more engineering - oriented ...
... recommended to provide readers with the tools to deal with diverse problems of analysis and prevention . However , the essential elements of electrochemical corrosion are presented in Chapter 1 , and the more engineering - oriented ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints