... Plating Bath Effects The other major factor which affects the porosity of an electrodeposit is the way in which it is plated . This includes both the composition of the electrolyte and the way in which it is used . It is not surprising ...
... Plating Bath Effects The other major factor which affects the porosity of an electrodeposit is the way in which it is plated . This includes both the composition of the electrolyte and the way in which it is used . It is not surprising ...
Page 272
... Plating , 35 ( 9 ) , 917 ( 1948 ) . 3 . N. Thon , D. Kelemen and L. Yang , Plating , 36 ( 4 ) , 362 ( 1949 ) . 4 . N. Thon , D. Kelemen and L. Yang , Plating , 36 ( 9 ) , 928 ( 1949 ) and 36 ( 11 ) , 1145 ( 1949 ) . 5 . N. Thon , L ...
... Plating , 35 ( 9 ) , 917 ( 1948 ) . 3 . N. Thon , D. Kelemen and L. Yang , Plating , 36 ( 4 ) , 362 ( 1949 ) . 4 . N. Thon , D. Kelemen and L. Yang , Plating , 36 ( 9 ) , 928 ( 1949 ) and 36 ( 11 ) , 1145 ( 1949 ) . 5 . N. Thon , L ...
Page 276
... Plating , 41 ( 5 ) , 503 ( 1954 ) . 13. D.G. Foulke and J.M. Tobin , Proc . A.E.S. , 43 , 234 ( 1956 ) . 14 . R.P. Diehl , Plating , 57 ( 1 ) , 51 ( 1970 ) . 15 . 16 . 17 . 18 . 19 . K.G. Ashurst and R.W. Neale , Trans . I.M.F. , 45 ...
... Plating , 41 ( 5 ) , 503 ( 1954 ) . 13. D.G. Foulke and J.M. Tobin , Proc . A.E.S. , 43 , 234 ( 1956 ) . 14 . R.P. Diehl , Plating , 57 ( 1 ) , 51 ( 1970 ) . 15 . 16 . 17 . 18 . 19 . K.G. Ashurst and R.W. Neale , Trans . I.M.F. , 45 ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints