Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 57
Page 344
... paints with the same zinc content in the dry film have different PVC values ; the epoxy paint will show the lower value . This would imply that for ethyl silicate paints the binder volume necessary to agglutinate the same number of zinc ...
... paints with the same zinc content in the dry film have different PVC values ; the epoxy paint will show the lower value . This would imply that for ethyl silicate paints the binder volume necessary to agglutinate the same number of zinc ...
Page 355
... paint arises from a narrow paint strip adjacent to the limiting steel bare surface / 40 / . For the second stage two theories have been proposed to explain the protective action of paint film : a ) blocking of the pores by the action of ...
... paint arises from a narrow paint strip adjacent to the limiting steel bare surface / 40 / . For the second stage two theories have been proposed to explain the protective action of paint film : a ) blocking of the pores by the action of ...
Page 357
... paint film behaves as a porous electrode . = The electrical resistance measurements of these paint films employing direct current in a 0.1 M sodium chloride solution ( pH = 7 ; Fig . 3 ) show that the resistance increases with the ...
... paint film behaves as a porous electrode . = The electrical resistance measurements of these paint films employing direct current in a 0.1 M sodium chloride solution ( pH = 7 ; Fig . 3 ) show that the resistance increases with the ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints