Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 84
Page 34
... metal , the expected state that the metal is in and the rate at which the metal proceeds to that state . Thermodynamics ad- dresses the first question . The potential - pH diagrams originally de- veloped by Pourbaix / 6 / are a ...
... metal , the expected state that the metal is in and the rate at which the metal proceeds to that state . Thermodynamics ad- dresses the first question . The potential - pH diagrams originally de- veloped by Pourbaix / 6 / are a ...
Page 48
... Metal - Metal Metal - Non Metal Metal Marine Growth Galvanically Protected Crevice Geometry Gap Depth Passive Current Film Stability Alloy Composition Major Constituent Minor Additions Impurities Total Geometry Exterior to Interior ...
... Metal - Metal Metal - Non Metal Metal Marine Growth Galvanically Protected Crevice Geometry Gap Depth Passive Current Film Stability Alloy Composition Major Constituent Minor Additions Impurities Total Geometry Exterior to Interior ...
Page 97
... metal Sandvik SAF 2507 plates , Heat No. 764296 , 18 mm Joint preparation and build - up sequence Impact strength ( full size specimen / average of three ) KV ( J ) Lateral expansion ( mm ) RT 40 ° C RT -40 ° C Weld metal 58 39 0.91 ...
... metal Sandvik SAF 2507 plates , Heat No. 764296 , 18 mm Joint preparation and build - up sequence Impact strength ( full size specimen / average of three ) KV ( J ) Lateral expansion ( mm ) RT 40 ° C RT -40 ° C Weld metal 58 39 0.91 ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints