for Aqueous Systems 4. MECHANISM OF INHIBITION The mechanism of action of passivators has been the subject of much controversy . The present theories of corrosion inhibition can be broadly classified in two groups . The action of ...
for Aqueous Systems 4. MECHANISM OF INHIBITION The mechanism of action of passivators has been the subject of much controversy . The present theories of corrosion inhibition can be broadly classified in two groups . The action of ...
Page 167
... mechanism of passivation . Uhlig and Geary / 41 / showed a linear relationship between C / AE vs. C ( where C = concentration of chromate ions , AE = change of potential ) and conformed to the Langmuir isotherm . The evidence gathered ...
... mechanism of passivation . Uhlig and Geary / 41 / showed a linear relationship between C / AE vs. C ( where C = concentration of chromate ions , AE = change of potential ) and conformed to the Langmuir isotherm . The evidence gathered ...
Page 171
... mechanism is the same for both types of steels . The presence or absence of dissolved oxygen in the solution does not place limitations on the elementary mechanism of the inhibition by molybdate ions . 4.4 Influence of Inclusion ...
... mechanism is the same for both types of steels . The presence or absence of dissolved oxygen in the solution does not place limitations on the elementary mechanism of the inhibition by molybdate ions . 4.4 Influence of Inclusion ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints