Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 40
Page 33
... limited tests conducted in the laboratory . Laboratory tests are at best simulations of the actual field ser- vice . There is no way to guarantee that all conditions , e.g. flow ef- fects , temperature distribution , concentration ...
... limited tests conducted in the laboratory . Laboratory tests are at best simulations of the actual field ser- vice . There is no way to guarantee that all conditions , e.g. flow ef- fects , temperature distribution , concentration ...
Page 55
... Limited knowledge of the chemistry of the pro- cess stream and of the corrosion process means that the relation- ship between B and the actual Tafel slopes may not be known . This uncertainty is not limited to electrochemical impedance ...
... Limited knowledge of the chemistry of the pro- cess stream and of the corrosion process means that the relation- ship between B and the actual Tafel slopes may not be known . This uncertainty is not limited to electrochemical impedance ...
Page 68
... limited time , limited re- sources , limited amounts of fluid , and toxicity concerns can force the corrosion practitioner to use a small laboratory type of appara- tus to simulate plant flow conditions . The following discussion cen ...
... limited time , limited re- sources , limited amounts of fluid , and toxicity concerns can force the corrosion practitioner to use a small laboratory type of appara- tus to simulate plant flow conditions . The following discussion cen ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/mē zinc zinc powder zinc-ethyl silicate paints