ABSTRACT The effect of laser surface treatment for generation of corrosion resistant coatings on 1045 steel has been studied . Various ways of surface alloying have been investigated by using continuous CO2 laser beam : i ) irradiation ...
ABSTRACT The effect of laser surface treatment for generation of corrosion resistant coatings on 1045 steel has been studied . Various ways of surface alloying have been investigated by using continuous CO2 laser beam : i ) irradiation ...
Page 283
... laser treatment . By producing changes in the structure of surface layers , laser beam irradiation can , in principle , affect various structure sensitive properties , including corrosion resistance . A greater possibility is , however ...
... laser treatment . By producing changes in the structure of surface layers , laser beam irradiation can , in principle , affect various structure sensitive properties , including corrosion resistance . A greater possibility is , however ...
Page 326
melt zone bulk Fig . 33 : Cross - sectional view of double laser treated specimen with powder injection during the first treatment . Irradiation conditions : 5 KW , 2 cm / sec . , 40 mm defocusing , beam shift 1 mm . specimen in 0.1N ...
melt zone bulk Fig . 33 : Cross - sectional view of double laser treated specimen with powder injection during the first treatment . Irradiation conditions : 5 KW , 2 cm / sec . , 40 mm defocusing , beam shift 1 mm . specimen in 0.1N ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/mē zinc zinc powder zinc-ethyl silicate paints